Printing Parameters
Nozzle Temperature: 210–250°C
Bed Temperature: 90–110°C
Bed Modification: PP bed sheet, Tape, or specialized PP glue
Active Cooling Fan: 50–100%
Layer Height: 0.2 mm
Shell Thickness: ≥ 0.8 mm
Print Speed: ≤ 200 mm/s
Note: Settings are based on a 0.4mm nozzle.
Description
Ultra-Low Density: Featuring a density of 0.90–0.92 g/cm³, this material produces exceptionally lightweight parts, offering noticeable weight savings compared to standard PLA or ABS.
Low Water Absorption: Highly hydrophobic base polymer resists moisture uptake, eliminating print bubbling and preventing hydration-related degradation during storage.
High Flexibility & Durability: Delivers superior impact energy absorption and fatigue resistance, preventing brittle fracture under heavy repetitive stress.
Excellent Chemical Resistance: Withstands harsh chemical environments, including exposure to common solvents, industrial oils, acids, and alkaline solutions.
Superior Interlayer Adhesion: Excellent thermal fusion between layers minimizes structural anisotropy and prevents Z-axis delamination under load.
Technical Datasheet
Melt Flow Rate (MFR): 2–8 g/10min¹ (ISO 1133)
Heat Deflection Temperature (HDT): 58°C² (ISO 75)
Vicat Softening Temperature (VST): 98°C³ (ISO 306)
Density: 0.90–0.92 g/cm³ (ISO 1183)
Odor: Low odor
Solubility: Insoluble in water
Note: ¹ Test conditions: T= 190℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.
Applications