THE K6™ PLA

Nozzle Temperature: 200–240°C

Bed Temperature: 35–55°C

Bed Modification: PEI frosted board

Active Cooling Fan: ON, 50–100%

Layer Height: 0.2 mm

Shell Thickness: ≥ 0.8 mm

Print Speed: ≤ 300 mm/s

Note: Settings are based on a 0.4mm nozzle.

Ultra-High Impact Strength Engineered with advanced modification to achieve exceptional toughness—notched impact strength reaches over 6x compared to raw PLA, handling extreme mechanical stress.

Engineering-Grade Toughness Pushes PLA beyond aesthetic models, delivering injection-mold-level durability capable of replacing functional engineering materials for load-bearing and structural parts.

Hassle-Free Printing & Zero Warping Retains all the signature advantages of PLA—effortless printability, zero warping, and consistent dimensional accuracy across all model sizes.

Superior Interlayer Bonding Delivers maximum layer adhesion, ensuring printed parts maintain high structural integrity and won't split along layer lines under impact.

Melt Temperature: ~160°C (ISO 11357)

Glass Transition Temperature: ~60°C (ISO 11357)

Melt Flow Rate (MFR): 2–7 g/10min¹ (ISO 1133)

Heat Deflection Temperature (HDT): 53°C² (ISO 75)

Vicat Softening Temperature (VST): 71°C³ (ISO 306)

Density: 1.17–1.19 g/cm³ (ISO 1183)

Odor: Odorless

Solubility: Insoluble in water

Note: ¹ Test conditions: T= 190℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.