THE K10™ PPS CF10
Features
- High Mechanical Strength
- Exceptional Rigidity
- 200°C+ Heat Resistance
- Low Thermal Shrinkage
- Inherent Flame Retardancy
- Superior Dimensional Stability
THE K10™ PPS CF10 是一种高性能碳纤维增强聚苯硫醚材料。其出色的强度、刚度和耐热性使其成为要求苛刻的应用的理想选择。这种材料可以承受超过 200°C 的连续使用，并保持出色的尺寸稳定性。其固有的阻燃性进一步增强了其在汽车和航空航天等领域的高压部件中的适用性。
推荐打印参数
| 喷头温度 | 230 ~ 260℃ |
| 底板温度 | 70 ~ 80℃ |
| 底板调整 | PEI frosted board |
| 冷却风扇 | 0 ~ 50% |
| 层高 | 0.2mm |
| 壳体厚度 | ≥ 0.8mm |
| 打印速度 | ≤ 200mm/s |
产品技术文档(TDS)
| 材料特性 | 参考值 | 测试方法 |
|---|---|---|
| 玻璃化转变温度(MFR)¹ | 10~20g/10min | ISO 1133 |
| 热挠曲温度/热变形 (HDT)² | 257℃ | ISO 75 |
| 维卡软化温度(VST)³ | 271.9℃ | ISO 306 |
| 密度 | 1.31~1.33g/cm³ | ISO 1183 |
| 气味 | 无味 | / |
| 溶解度 | 不溶于水 | / |
Printing Parameters
Nozzle Temperature: 285–320°C
Bed Temperature: 100–120°C
Bed Modification: Tape or glue
Active Cooling Fan: 0–50%
Layer Height: 0.2 mm
Shell Thickness: ≥ 0.8 mm
Print Speed: ≤ 250 mm/s
Note: Settings are based on a 0.4mm nozzle.
Description
High Mechanical Strength: Provides superior load-bearing capacity for heavy-duty structural components.
Exceptional Rigidity: Offers outstanding stiffness to maintain structural integrity under high stress.
200°C+ Heat Resistance: Maintains structural stability in extreme thermal environments exceeding 200°C.
Low Thermal Shrinkage: Minimizes warping and residual stress during the printing and cooling process.
Inherent Flame Retardancy: Formulated with self-extinguishing flame-retardant properties for elevated safety.
Superior Dimensional Stability: Ensures strict tolerance adherence and minimal thermal expansion in demanding applications.
Technical Datasheet
Melt Flow Rate (MFR): 10–20 g/10min¹ (ISO 1133)
Heat Deflection Temperature (HDT): 257°C² (ISO 75)
Vicat Softening Temperature (VST): 271.9°C³ (ISO 306)
Density: 1.31–1.33 g/cm³ (ISO 1183)
Odor: Odorless
Solubility: Insoluble in water
Note: ¹ Test conditions: T= 300℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.
Applications