THE K6™ PLA CF10

Nozzle Temperature: 200–240°C

Bed Temperature: 35–55°C

Bed Modification: PEI frosted board

Active Cooling Fan: ON, 50–100%

Layer Height: 0.2 mm

Shell Thickness: ≥ 0.8 mm

Print Speed: ≤ 250 mm/s

Note: Settings are based on a 0.4mm nozzle.

Carbon Fiber Reinforced Strength Infused with 10% premium carbon fiber to deliver exceptional structural rigidity, high tensile strength, and superior dimensional stability.

Perfect Balance of Strength, Stiffness & Toughness Expertly modified to bridge performance and usability, avoiding the brittleness of standard CF composites while maintaining high structural load capacity.

Ideal Entry-Level CF Composite Combines the smooth printability and low warping of PLA with composite performance—making it the perfect, hassle-free choice for stepping into carbon fiber 3D printing.

Premium Matte Surface & Hidden Layer Lines Produces an attractive matte finish with highly masked layer lines, ideal for sleek functional prototypes, structural parts, and high-end aesthetic models.

Melt Temperature: ~160°C (ISO 11357)

Glass Transition Temperature: ~60°C (ISO 11357)

Melt Flow Rate (MFR): 2–7 g/10min¹ (ISO 1133)

Heat Deflection Temperature (HDT): 58°C² (ISO 75)

Vicat Softening Temperature (VST): 71°C³ (ISO 306)

Density: 1.10–1.12 g/cm³ (ISO 1183)

Odor: Odorless

Solubility: Insoluble in water

Note: ¹ Test conditions: T= 190℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.