THE K6™ PLA
Color
红色
Weight
Diameter
- Ultra-High Impact Strength Engineered with advanced modification to achieve exceptional toughness—notched impact strength reaches over 6x compared to raw PLA, handling extreme mechanical stress.
- Engineering-Grade Toughness Pushes PLA beyond aesthetic models, delivering injection-mold-level durability capable of replacing functional engineering materials for load-bearing and structural parts.
- Hassle-Free Printing & Zero Warping Retains all the signature advantages of PLA—effortless printability, zero warping, and consistent dimensional accuracy across all model sizes.
- Superior Interlayer Bonding Delivers maximum layer adhesion, ensuring printed parts maintain high structural integrity and won't split along layer lines under impact.
Suggested Printing Parameters
| Nozzle temperature | 200 ~ 240℃ |
| Bed temperature | 35 ~ 55℃ |
| Bed modification | PEI frosted board |
| Active cooling fan | ON,50~100% |
| Layer height | 0.2mm |
| Shell thickness | ≥ 0.8mm |
| Print speed | ≤ 300mm/s |
Technical Data Sheet (TDS)
| Material Properties | Typical Value | Test Method |
|---|---|---|
| Melt temperature | ~160℃ | ISO 11357 |
| Glass transition temperature | ~60℃ | ISO 11357 |
| Melt flow rate (MFR)¹ | 2~7g/10min | ISO 1133 |
| Heat deflection temperature (HDT)² | 53℃ | ISO 75 |
| Vicat softening temperature (VST)³ | 71℃ | ISO 306 |
| Density | 1.17~1.19g/cm³ | ISO 1183 |
| Odor | Odorless | / |
| Solubility | Insoluble in water | / |