THE K5™ PETG Rapid

Color
奶油绿
Weight
Diameter
Description
  • Ultra-Fast High-Speed Printing Engineered for next-gen high-speed printers, supporting continuous, stable printing at 300mm/s and peak speeds up to 400mm/s without sacrificing quality.
  • Enhanced Fluidity & Rapid Cooling Features optimized melt flow and accelerated cooling dynamics, preventing stringing and sagging even during ultra-fast extrusion cycles.
  • Strength, Flexibility & Heat Resistance Combines rapid printing capabilities with PETG’s signature mechanical durability, impact toughness, and high thermal stability.
  • Flawless Layer Adhesion & Surface Quality Delivers excellent bond strength between layers and smooth surface finishes on complex models, even at high volumetric speeds.
Temperature Resistance Strength Toughness Rigidity Ease of Printing Z-axis Strength

Suggested Printing Parameters

Nozzle temperature 235 ~ 275℃
Bed temperature 60 ~ 80℃
Bed modification PEI frosted board
Active cooling fan 0~50%
Layer height 0.2mm
Shell thickness ≥ 0.8mm
Print speed ≤ 300mm/s
Settings are based on a 0.4mm nozzle.

Technical Data Sheet (TDS)

Material Properties Typical Value Test Method
Glass transition temperature ~66℃ ISO 11357
Melt flow rate (MFR)¹ 5~10g/10min ISO 1133
Heat deflection temperature (HDT)² 70℃ ISO 75
Vicat softening temperature (VST)³ 83℃ ISO 306
Density 1.29~1.31g/cm³ ISO 1183
Odor Low odor /
Solubility Insoluble in water /

1. Test conditions: T= 230℃; m= 2.16kg.

2. Test conditions: 0.45MPa; 120℃/h.

3. Test conditions: 10N; 120℃/h.

Download TDS
Download Brochure
Download Print Profiles

THE K5™ PETG Rapid has passed the following certifications: RoHS China, California Proposition 65(CP65), TSCA, EU RoHS, UK RoHS, REACH SVHC.