THE K11™ PEKK
Color
自然色
Weight
THE K11™ PEKK is a high-performance PEKK material with a low crystallization rate. This unique characteristic results in transparent, amorphous printed parts. Its inherent flame resistance, high-temperature tolerance, and exceptional strength contribute to producing parts with superior interlayer adhesion, particularly in the Z-axis direction. This makes PEKK an ideal choice for applications demanding high strength and durability.
Suggested Printing Parameters
| Nozzle temperature | 360 ~ 390℃ |
| Bed temperature | 120 ~ 170℃ |
| Chamber temperature | 90 ~ 160℃ |
| Bed modification | NO |
| Active cooling fan | 0~100% |
| Layer height | 0.2mm |
| Shell thickness | ≥ 0.8mm |
| Print speed | 30~60mm/s |
Technical Data Sheet (TDS)
| Material Properties | Typical Value | Test Method |
|---|---|---|
| Melt temperature (HDT)² | ~340℃ | ISO 11357 |
| Melt flow rate (MFR)¹ | 6~8g/10min | ISO 1133 |
| Heat deflection temperature (HDT)² | 150℃(before annealing)/ 182℃(after annealing) | ISO 75 |
| Vicat softening temperature (VST)³ | 157.8℃ | ISO 306 |
| Density | 1.28g/cm³ | ISO 1183 |
| Odor | Odorless | / |
| Solubility | Insoluble in water | / |