K5™ PLA Tee

1 kg

1.75mm

Nozzle Temperature: 190~230°C

Bed Temperature: 35–55°C

Bed Modification: PEI frosted board

Active Cooling Fan: ON, 50–100%

Layer Height: 0.2 mm

Shell Thickness: ≥ 0.8 mm

Print Speed: ≤ 260 mm/s

Note: Settings are based on a 0.4mm nozzle.

Recycled Tea Grounds & Unique Effect: Infused with upcycled tea waste to create a realistic, unique visual and tactile texture.

Smooth Extrusion: Uniform fiber distribution ensures stable, continuous printing without clogging.

Tea Aroma: Releases a subtle tea fragrance while printing.

Eco-Friendly PLA Base: Developed in collaboration with Master Kong (康师傅) for sustainable material performance.

Melt Temperature: ~165°C (ISO 11357)

Glass Transition Temperature: ~60°C (ISO 11357)

Melt Flow Rate (MFR): 2–8 g/10min¹ (ISO 1133)

Heat Deflection Temperature (HDT): 50-60°C² (ISO 75)

Vicat Softening Temperature (VST): 60-65°C³ (ISO 306)

Density: 1.4-1.45g/cm³ (ISO 1183)

Odor: Tea

Solubility: Insoluble in water

Note: ¹ Test conditions: T= 190℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.