DER K11™ PEEK GF10
Features
- Glass Fiber Reinforcement
- Lightweight Metal Replacement
- High Strength & Rigidity
- Higher Density & Toughness
- Excellent Heat Resistance
- Broad Chemical Resistance
- Inherent Flame Resistance
Das K11™ PEEK GF10 ist ein glasfaserverstärktes PEEK-Material mit hoher Festigkeit und Steifigkeit sowie Hitzebeständigkeit. Anstelle von Metallteilen in vielen Anwendungen sind gedruckte Teile leicht und stark, deren Funktionen denen von PEEK K10CF ähneln, jedoch mit höherer Dichte und Zähigkeit.
Empfohlene Druckparameter
| Düsatemperatur | 400 ~ 450℃ |
| Betttemperatur | 110 ~ 220℃ |
| Kammertemperatur | 80 ~ 220℃ |
| Bettmodifikation | NEIN & Hochtemperaturkleber |
| Aktiver Lüfter | AUS |
| Schichthöhe | 0.2mm |
| Schalenstärke | ≥ 0.8mm |
| Druckgeschwindigkeit | 30~60mm/s |
Technisches Datenblatt (TDS)
| Materialeigenschaften | Typischer Wert | Prüfmethode |
|---|---|---|
| Schmelztemperatur (HDT)² | ~340℃ | ISO 11357 |
| Schmelzflussindex (MFR)¹ | 10~15g/10min | ISO 1133 |
| Wärmeformbeständigkeit (HDT)² | 202℃ | ISO 75 |
| Vicat-Erweichungstemperatur (VST)³ | / | ISO 306 |
| Dichte | 1.28g/cm³ | ISO 1183 |
| Geruch | Geruchlos | / |
| Löslichkeit | Unlöslich in Wasser | / |
Printing Parameters
Nozzle Temperature: 400–450°C
Bed Temperature: 110–220°C
Chamber Temperature: 80–220°C
Bed Modification: NO & High temperature glue
Active Cooling Fan: OFF
Layer Height: 0.2 mm
Shell Thickness: ≥ 0.8 mm
Print Speed: 30–60 mm/s
Note: Settings are based on a 0.4mm nozzle. A hardened steel or ruby nozzle is highly recommended to prevent premature wear from glass fibers.
Description
Glass Fiber Reinforcement: Micro-glass fiber compounding provides balanced structural reinforcement and isotropic stability.
Lightweight Metal Replacement: High mechanical strength and stiffness-to-weight ratio make it ideal for replacing traditional die-cast metals.
High Strength & Rigidity: Enhanced flexural and tensile modulus engineered for heavy structural loads under harsh environments.
Higher Density & Toughness: Delivers superior impact energy absorption and density balance compared to unreinforced high-temp polymers.
Excellent Heat Resistance: Exceptional thermal endurance with a Heat Deflection Temperature (HDT) reaching up to 202°C.
Broad Chemical Resistance: Highly resistant to harsh chemicals, industrial solvents, hydraulic fluids, and strong acids or bases.
Inherent Flame Resistance: Natural UL94 V-0 level flame retardancy without relying on flame-retardant additives.
Technical Datasheet
Melt Temperature: ~340°C (ISO 11357)
Melt Flow Rate (MFR): 10–15 g/10min¹ (ISO 1133)
Heat Deflection Temperature (HDT): 202°C² (ISO 75)
Vicat Softening Temperature (VST): N/A³ (ISO 306)
Density: 1.28 g/cm³ (ISO 1183)
Odor: Odorless
Solubility: Insoluble in water
Note: ¹ Test conditions: T= 380℃; m= 5kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.