DAS K6™ PLA FG
Features
- Food-Contact Safe
- Magnetically Detectable
- High Dimensional Stability
- Good Mechanical Strength
- Easy & Smooth Printability
Dieses lebensmittelechte PLA ist sicher für den Kontakt mit Lebensmitteln und Getränken. Es wird nach strengen Sicherheitsstandards hergestellt und ist daher ideal für den Druck von individuellen Küchenutensilien und Lebensmittelbehältern.
Empfohlene Druckparameter
| Düs temperatur | 200 ~ 230℃ |
| Betttemperatur | 35 ~ 55℃ |
| Bettenumbau | PEI-mattierte Platine |
| Aktiver Kühlventilator | EIN, 50~100% |
| Schichthöhe | 0.2mm |
| Wandstärke | ≥ 0.8mm |
| Druckgeschwindigkeit | ≤ 300mm/s |
Technisches Datenblatt (TDS)
| Materialeigenschaften | Typischer Wert | Testmethode |
|---|---|---|
| Schmelztemperatur | ~160℃ | ISO 11357 |
| Glasübergangstemperatur | ~60℃ | ISO 11357 |
| Schmelzflussrate (MFR)¹ | 3~7g/10min | ISO 1133 |
| Wärmeformbeständigkeit (HDT)² | 61℃ | ISO 75 |
| Vicat-Erweichungstemperatur (VST)³ | 67℃ | ISO 306 |
| Dichte | 1.30~1.35g/cm³ | ISO 1183 |
| Geruch | Geruchlos | / |
| Löslichkeit | Wasserunlöslich | / |
Printing Parameters
Nozzle Temperature: 200–230°C
Bed Temperature: 35–55°C
Bed Modification: PEI frosted board
Active Cooling Fan: ON, 50–100%
Layer Height: 0.2 mm
Shell Thickness: ≥ 0.8 mm
Print Speed: ≤ 300 mm/s
Note: Settings are based on a 0.4mm nozzle.
Description
Food-Contact Safe: Formulated with food-grade compliant raw materials, suitable for functional applications requiring contact with food items.
Magnetically Detectable: Embedded with specialized additives that allow stray particles or broken components to be easily picked up by industrial metal/magnetic detectors to prevent product contamination.
High Dimensional Stability: Maintains precise tolerances and low deformation during printing, making it ideal for accurate structural parts and factory jigs.
Good Mechanical Strength: Offers reliable tensile and impact resistance for daily industrial testing, wear parts, and functional components.
Easy & Smooth Printability: Features excellent flowability and low warping, delivering a seamless printing experience comparable to standard PLA.
Technical Datasheet
Melt Temperature: ~160°C (ISO 11357)
Glass Transition Temperature: ~60°C (ISO 11357)
Melt Flow Rate (MFR): 3–7 g/10min¹ (ISO 1133)
Heat Deflection Temperature (HDT): 61°C² (ISO 75)
Vicat Softening Temperature (VST): 67°C³ (ISO 306)
Density: 1.30–1.35 g/cm³ (ISO 1183)
Odor: Odorless
Solubility: Insoluble in water
Note: ¹ Test conditions: T= 190℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.
Applications