Technical Data Sheet (TDS)

Material Properties	Typical Value	Test Method
Melt temperature	~340℃	ISO 11357
Melt flow rate (MFR)¹	6~8g/10min	ISO 1133
Heat deflection temperature (HDT)²	150℃(before annealing)/ 182℃(after annealing)³	ISO 75
Vicat softening temperature (VST)³	157.8℃	ISO 306
Density	1.28g/cm³	ISO 1183
Odor	Odorless	/
Solubility	Insoluble in water	/

        Suggested Printing Parameters
    
                Nozzle temperature
                360 ~ 390℃
            
                Bed temperature
                120 ~ 170℃
            
                Chamber temperature
                90 ~ 160℃
            
                Bed modification
                NO
            
                Active cooling fan
                0~100%
            
                Layer height
                0.2mm
            
                Shell thickness
                ≥ 0.8mm
            
                Print speed
                30~60mm/s
            
        Settings are based on a 0.4mm nozzle.

Color Selector

Select a color

Weight options:

: 250g, 500g, 1kg

THE K11™ PEKK

THE K11™ PEKK is a high-performance PEKK material with a low crystallization rate. This unique characteristic results in transparent, amorphous printed parts. Its inherent flame resistance, high-temperature tolerance, and exceptional strength contribute to producing parts with superior interlayer adhesion, particularly in the Z-axis direction. This makes PEKK an ideal choice for applications demanding high strength and durability.