THE K8™ BAS 90

Nozzle Temperature: 250-290°C

Bed Temperature: 90~110°C

Bed Modification: PEI frosted board

Active Cooling Fan: 0%~50%

Layer Height: 0.2 mm

Shell Thickness: ≥ 0.8 mm

Print Speed: ≤100 mm/s

Note: Settings are based on a 0.4mm nozzle.

Dedicated Support for PA: Engineered specifically for PA, PA-CF, and PA-GF to ensure optimal adhesion and clean interface separation.

Easy Removal: Enables effortless break-away support removal without damaging the main printed part or leaving heavy surface marks.

Wide Compatibility: Works seamlessly with a broad spectrum of PA-series materials for versatile high-performance 3D printing.

Dual & Single Nozzle Ready: Fully compatible with both dual-nozzle setups and single-nozzle multi-color/multi-material system printing.

Complex Structure Stability: Delivers exceptional structural integrity during printing to guarantee precise results for intricate geometries.

Melt Flow Rate (MFR): 21~27 g/10min¹ (ISO 1133)

Heat Deflection Temperature (HDT)²: 71°C (ISO 75)

Vicat Softening Temperature (VST)³: 78°C (ISO 306)

Density: 1.34~1.36 g/cm³ (ISO 1183)

Odor: Odorless

Solubility: Insoluble in water

Note: ¹ Test conditions: T= 230℃; m= 2.16kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.