THE K11™ PEEK GF10

Nozzle Temperature: 400–450°C

Bed Temperature: 110–220°C

Chamber Temperature: 80–220°C

Bed Modification: NO & High temperature glue

Active Cooling Fan: OFF

Layer Height: 0.2 mm

Shell Thickness: ≥ 0.8 mm

Print Speed: 30–60 mm/s

Note: Settings are based on a 0.4mm nozzle. A hardened steel or ruby nozzle is highly recommended to prevent premature wear from glass fibers.

Glass Fiber Reinforcement: Micro-glass fiber compounding provides balanced structural reinforcement and isotropic stability.

Lightweight Metal Replacement: High mechanical strength and stiffness-to-weight ratio make it ideal for replacing traditional die-cast metals.

High Strength & Rigidity: Enhanced flexural and tensile modulus engineered for heavy structural loads under harsh environments.

Higher Density & Toughness: Delivers superior impact energy absorption and density balance compared to unreinforced high-temp polymers.

Excellent Heat Resistance: Exceptional thermal endurance with a Heat Deflection Temperature (HDT) reaching up to 202°C.

Broad Chemical Resistance: Highly resistant to harsh chemicals, industrial solvents, hydraulic fluids, and strong acids or bases.

Inherent Flame Resistance: Natural UL94 V-0 level flame retardancy without relying on flame-retardant additives.

Melt Temperature: ~340°C (ISO 11357)

Melt Flow Rate (MFR): 10–15 g/10min¹ (ISO 1133)

Heat Deflection Temperature (HDT): 202°C² (ISO 75)

Vicat Softening Temperature (VST): N/A³ (ISO 306)

Density: 1.28 g/cm³ (ISO 1183)

Odor: Odorless

Solubility: Insoluble in water

Note: ¹ Test conditions: T= 380℃; m= 5kg. ² Test conditions: 0.45MPa; 120℃/h. ³ Test conditions: 10N; 120℃/h.